PAF-300-8
$0.00
Sensitivity: Kodak step tablet 14 steps at 250mJ/cm² / 7 steps; Flexibility: Bending 180 degrees (on Polyimide 25μm) / 20 times; Warpage: Size 50x50mm (on Polyimide 25μm) / 12mm; Film hardness: JIS K5400 / 3H; Adhesion: On polyimide / 100/100, On copper / 100/100; Acid Resistance: 10% HCl for 15 minutes, tape peeling test / No peeling; Solvent Resistance: IPA for 30 minutes, tape peeling test / No peeling; Resolution: On polyimide (25μm) / 50μm, On Cu of two-layer CCL (Cu:18μm, PI:25μm) / 40μm; Heat test (HBBT): 85°C, 85%RH / 1,000 hours, 1,000h OK; UL: UL 94 / VTM-0 rating; Tg (TMA): 5055°C; Physical values: Breaking strength / 1520MPa, Elongation / 3545%, Elastic modulus / 1.0~1.1GPa.
Description
Sensitivity: Kodak step tablet 14 steps at 250mJ/cm² / 7 steps; Flexibility: Bending 180 degrees (on Polyimide 25μm) / 20 times; Warpage: Size 50x50mm (on Polyimide 25μm) / 12mm; Film hardness: JIS K5400 / 3H; Adhesion: On polyimide / 100/100, On copper / 100/100; Acid Resistance: 10% HCl for 15 minutes, tape peeling test / No peeling; Solvent Resistance: IPA for 30 minutes, tape peeling test / No peeling; Resolution: On polyimide (25μm) / 50μm, On Cu of two-layer CCL (Cu:18μm, PI:25μm) / 40μm; Heat test (HBBT): 85°C, 85%RH / 1,000 hours, 1,000h OK; UL: UL 94 / VTM-0 rating; Tg (TMA): 5055°C; Physical values: Breaking strength / 1520MPa, Elongation / 3545%, Elastic modulus / 1.0~1.1GPa.